Ooru idabobo ọra rinhoho Lo ninu Windows
Apẹrẹ I, apẹrẹ C, apẹrẹ T, apẹrẹ CT ati apẹrẹ HK jẹ apẹrẹ ti o wọpọ julọ, a tun le ni ibamu si awọn ibeere onibara tabi awọn aworan lati ṣe atunṣe apẹrẹ pataki miiran.
1.Effectively pọ gbona ninu awọn eto ohun ini idabobo.
2.Dinku condensation lori window.
3.Sound idabobo.
4.Imudara itunu ati ipo igbe.
5.Possible ė awọ ti a bo pese dara darapupo ipa.
6.Various awọn apẹrẹ yoo jẹ apẹrẹ fun awọn ibeere onibara.
7.The ṣiṣẹ otutu ti awọn gbona idabobo rinhoho ni 220 ° C, Melting Point Gigun si 246 ° C.Eyi jẹ ki ilana ti a bo lẹhin apejọ awọn profaili akojọpọ.
8.High corrosion-resistance, ojo-resistance, ooru-resistance, alkali-resistance ati ki o gun aye ti lilo.
9.linear thermal dilation olùsọdipúpọ fẹrẹ jẹ aami ti awọn profaili aluminiomu.
| RARA. | Nkan | Ẹyọ | GB/T 23615.1-2009 | HC-Technical sipesifikesonu |
|
| Ohun elo Properties | |||
| 1 | iwuwo | g/cm3 | 1.3 ± 0.05 | 1.28-1.35 |
| 2 | Imugboroosi laini | K-1 | (2.3-3.5)× 10-5 | (2.3-3.5)× 10-5 |
| 3 | Vicat rirọ otutu | ºC | ≥230ºC | ≥233ºC |
| 4 | Oju yo (0.45MPa) | ºC | ≥240ºC | ≥240 |
| 5 | Idanwo fun awọn dojuijako fifẹ | - | Ko si dojuijako | Ko si dojuijako |
| 6 | Lile eti okun | - | 80±5 | 80-85 |
| 7 | Agbara ipa (Ti ko ṣe akiyesi) | KJ/m2 | ≥35 | ≥38 |
| 8 | Agbara fifẹ (ni gigun) | MPa | ≥80a | ≥82a |
| 9 | Iwọn rirọ | MPa | ≥4500 | ≥4550 |
| 10 | Elongation ni isinmi | % | ≥2.5 | ≥2.6 |
| 11 | Agbara fifẹ (ipopada) | MPa | ≥70a | ≥70a |
| 12 | Agbara fifẹ otutu ti o ga (iyipada) | MPa | ≥45a | ≥47a |
| 13 | Agbara fifẹ iwọn otutu kekere (iyipada) | MPa | ≥80a | ≥81a |
| 14 | Agbara fifẹ omi (iyipada) | MPa | ≥35a | ≥35a |
| 15 | Agbara fifẹ ti ogbo (iyipada) | MPa | ≥50a | ≥50a |
1.Sample akoonu omi ti o kere ju 0.2% nipasẹ iwuwo.
2.Norm yàrá majemu: (23 ± 2)ºC ati (50 ± 10)% ojulumo ọriniinitutu.
3.Awọn pato ti a samisi pẹlu "a" nikan kan si I-apẹrẹ rinhoho bibẹẹkọ, awọn alaye ti o pari laarin olupese ati olura nipasẹ ijumọsọrọ, yoo kọ ni adehun tabi aṣẹ rira.
Awọn ila naa yoo wa ni ipamọ ni agbegbe ventilated ati agbegbe gbigbẹ, ti a gbe ni ita, san ifojusi si mabomire, fifipamọ kuro ni orisun ooru, yago fun titẹ eru ati olubasọrọ pẹlu acid, alkali bi daradara bi ohun elo Organic.
A ni agbara iṣelọpọ ti awọn mita 100000 fun ọjọ kan.Fun awọn alaye ti o wọpọ, a ni awọn apẹrẹ, ati pe yoo firanṣẹ ni awọn ọjọ iṣẹ 15-20 lẹhin gbigba ohun idogo naa.